球形不锈钢、工模具钢粉末系列

采用真空气雾化工艺,氧含量低于300ppm,球形度好的球形粉末,可用于金属3D打印,注射成型,粉末冶金以及修复耐腐蚀性的工件.

不锈钢粉末主要技术性能

化学成分(%)
牌号 Ni Cr Fe Mo P S Ti Mn Si N Ac/Ta Cu C
304L 8.0-12.0 18.0-20.0 Bal / ≤0.045 ≤0.03 / ≤2.0 ≤0.75 ≤0.1 /   ≤0.03
316L 10.0-14.0 16.0-18.0 Bal 2.0-3.0 ≤0.045 ≤0.03 / ≤2.0 ≤0.75 ≤0.1 /   ≤0.08
316Ti 10.0-14.0 16.0-18.0 Bal 2.0-3.0 ≤0.045 ≤0.03 ≥5C%-0.7 ≤2.0 ≤0.75 ≤0.1 /   ≤0.08
317L 11.0-15.0 18.0-20.0 Bal 3.0-4.0 ≤0.045 ≤0.03 / ≤2.0 ≤0.75 ≤0.1 /   ≤0.08
F321 9.0-12.0 17.0-19.0 Bal / ≤0.035 ≤0.03 ≥5C% ≤2.0 ≤1.0 / /   ≤0.08
310 19.0-22.0 24.0-26.0 Bal / ≤0.045 ≤0.03 / ≤2.0 ≤1.5 / /   ≤0.25
310S 19.0-22.0 24.0-26.0 Bal / ≤0.045 ≤0.03 / ≤2.0 ≤1.5 / /   ≤0.08
310H 19.0-22.0 24.0-26.0 Bal / ≤0.045 ≤0.03 / ≤2.0 ≤0.75 / /   0.04-0.1
347 9.0-13.0 17.0-19.0 Bal / ≤0.045 ≤0.03 / ≤2.0 ≤0.75 / 10*(C+N)-1.0   ≤0.08
347H 9.0-13.0 17.0-19.0 Bal / ≤0.045 ≤0.03 / ≤2.0 ≤0.75 / 8*(C+N)-1.0   0.04-0.1
2205 4.5-6.5 22.5-23.0 Bal 3.2-3.5 ≤0.03 ≤0.15 / / ≤1.0 0.14-0.2 /   ≤0.03
904L 23.0-28.0 19.0-23.0 Bal 4.0-5.0 ≤0.045 ≤0.035 / ≤2.0 ≤1.0 / / 1.0-2.0

/

 采用真空气雾化工艺,可得到氧含量低于300ppm的球形粉末,粉末的粒度均匀,卫星球少,主要用于模具制造与修复、金属3D打印、刀具行业等领域、

工模具钢粉末主要的技术性能

化学成分(%):

牌号 C Si Mn Cr Mo V Fe
H13 0.32-0.45 0.8-1.2 0.2-0.5 4.75-5.5 1.1-1.75 0.8-1.2 Bal
T12 1.15-1.24 ≤0.35 ≤0.4       Bal

 

粉末性能:        
牌号 规格(um) 形貌 松装密度g/cm³ 霍尔流速   (s) 氧含量(ppm)
H13 15-53 球形 ≥4.0 ≤23 ≤300
53-106 球形 ≥4.1 ≤20 ≤300
T12 15-53 球形 ≥4.0 ≤23 ≤300
53-106 球形 ≥4.1 ≤20 ≤300